It is very easy to cause concrete cracking if the construction or maintenance are not done correctly. What are then the five main causes of cracking concrete?
1. The cement proportion problem: Some workers in construction will add more water for a more fluid concrete. However, this will result in an increase in water-cement ratio. This will cause the concrete to harden too quickly, and lead to cracking.
2. Transport and mixing issues: If mixing and transporting concrete takes too much time, the water in the concrete will evaporate quickly. concrete . The result is a concrete that cannot meet construction specifications, resulting in cracks in the concrete.
3. Construction speed
4. Maintenance is unreasonable. During the period of maintenance, if late watering isn't maintained, the result will be the Cracking phenomenon Later in the year, concrete will be used. Concrete is used in the future. Concrete Surface Watering You can water the concrete often to speed up the drying process. Concrete will shrink if it is not watered. Late cracking occurs when concrete strength is decreased.
5. Environmental factors: If the environment at the construction site is relatively dry and there is high temperature, wind, or both, then the evaporation rates of the concrete are accelerated. This results in cracks on the surface. Concrete constructions are most likely to crack in summer or winter due to the temperature difference.
Solution: Add a crack-preventing agent. A composite anti-cracking agents made of inorganic materials can prevent foam concrete from fracturing by more than 80%. Add 2 to 3 kilograms per cubic foot.
Inquiry us
PREVIOUS NEWS
NEXT NEWS
It is very easy to cause concrete cracking if the construction or maintenance are not done correctly. What are then the five main causes of cracking concrete? 1. The cement proportion problem: Some workers in construction will add more water for a mo…